Brass flat bars

Brass flat bar for industrial applications. Available in a wide selection of sizes according to customer needs.

Data sheet: Brass flat bars

Brass flat bars, also known as brass plates or flat bars, offer the unique combination of properties of the copper-zinc alloy in a format that is very useful for a wide range of industrial, construction and decorative applications. Unlike brass strips, flat bars are generally thicker and are used in situations requiring greater strength, stiffness or volume of material.

The characteristics of brass bars include mechanical strength and ductility, which allows them to be formed and machined. In addition, they also have a high load capacity, ideal for use as fasteners or supports. Their aesthetic finish is designed for decorative or architectural applications.

Copper-Zinc Alloys

Material Designation Composition in % (mass fraction) Density g/cm3
 Symbolic  Numerical Element Cu Al Fe Ni Pb Sn Zn Total other  approx.
CuZn36 CW507L min. 63,5 - - - - - Rest - 8,4
max. 65,5 0,02 0,05 0,3 0,05 0,1 - 0,1
CuZn37 CW508L min. 62 - - - - - Rest - 8,4
max. 64 0,05 0,1 0,3 0,1 0,1 - 0,1
CuZn40 CW509L min. 59,5 - - - - - Rest - 8,4
max. 61,5 0,05 0,2 0,3 0,3 0,2 - 0,2

COPPER - ZINC - LEAD ALLOYS

Material Designation Composition in % (mass fraction) Density g/cm3
Symbolic Numerical element Cu Al As Fe Mn Ni Pb Sn Zn total others approx.
CuZn35Pb1 CW600N min. 62,5 - - - - - 0,8 - Rest - 8,5
max. 64,0 0,05 - 0,1 - 0,3 1,6 0,1 - 0,1
CuZn35Pb2 CW601N min. 62,0 - - - - - 1,6 - Rest - 8,5
max. 63,5 0,05 - 0,1 - 0,3 2,5 0,1 - 0,1
CuZn36Pb3 CW603N min. 60,0 - - - - - 2,5 - Rest - 8,5
max. 62,0 0,05 - 0,3 - 0,3 3,5 0,2 - 0,2
CuZn37Pb2 CW606N min. 61,0 - - - - - 1,6 - Rest - 8,4
max. 62,0 0,05 - 0,2 - 0,3 2,5 0,2 - 0,2
CuZn38Pb1 CW607N min. 60,0 - - - - - 0,8 - Rest - 8,4
max. 61,0 0,05 - 0,2 - 0,3 1,6 0,2 - 0,2
CuZn38Pb2 CW608N min. 60,0 - - - - - 1,6 - Rest - 8,4
max. 61,0 0,05 - 0,2 - 0,3 2,5 0,2 - 0,2
CuZn38Pb4 CW609N min. 57,0 - - - - - 3,5 - Rest - 8,4
max. 59,0 0,05 - 0,3 - 0,3 4,2 0,3 - 0,2
CuZn39Pb0,5 CW610N min. 59,0 - - - - - 0,2 - Rest - 8,4
max. 60,5 0,05 - 0,2 - 0,3 0,8 0,2 - 0,2
CuZn39Pb1 CW611N min. 59,0 - - - - - 0,8 - Rest - 8,4
max. 60,0 0,05 - 0,2 - 0,3 1,6 0,2 - 0,2
CuZn39Pb2 CW612N min. 59,0 - - - - - 1,6 - Rest - 8,4
max. 60,0 0,05 - 0,3 - 0,3 2,5 0,3 - 0,2
CuZn39Pb3 CW614N min. 57,0 - - - - - 2,5 - Rest - 8,4
max. 59,0 0,05 - 0,3 - 0,3 3,5 0,3 - 0,2
CuZn40Pb2 CW617N min. 57,0 - - - - - 1,6 - Rest - 8,4
max. 59,0 0,05 - 0,3 - 0,3 2,5 0,3 - 0,2
CuZn43Pb2 CW623N min. 55,0 - - - - - 1,6 - Rest - 8,4
max. 57,0 0,05 - 0,3 - 0,3 3,0 0,3 - 0,2
CuZn36Pb2As CW602N min. 61 - 0,02 - - - 1,7 - Rest - 8,4
max. 63 0,05 0,15 0,1 0,1 0,3 2,8 0,1 - 0,2
CuZn39Pb2Sn CW613N min. 59 - - - - - 1,6 0,2 Rest - 8,4
max. 60 0,1 - 0,4 - 0,3 2,5 0,5 - 0,2
CuZn40Pb2Al CW618N min. 57 0,05 - - - - 1,6 - Rest - 8,3
max. 59 0,5 - 0,3 - 0,3 3 0,3 - 0,2
CuZn40Pb2Sn CW619N min. 57 - - - - - 1,6 0,2 Rest - 8,4
max. 59 0,1 - 0,4 - 0,3 2,5 0,5 - 0,2
CuZn41Pb1Al CW620N min. 57 0,05 - - - - 0,8 - Rest - 8,3
max. 59 0,5 - 0,3 - 0,3 1,6 0,3 - 0,2
CuZn42PbAL CW621N min. 57 0,05 - - - - 0,2 - Rest - 8,3
max. 59 0,5 - 0,3 - 0,3 0,8 0,3 - 0,2
CuZn43Pb1Al CW622N min. 55 0,05 - - - - 0,8 - Rest - 8,3
max. 57 0,5 - 0,3 - 0,3 1,6 0,3 - 0,2
CuZn43Pb2Al CW624N min. 55 0,05 - - - - 1,6 - Rest - 8,4
max. 57 0,5 - 0,3 - 0,3 3 0,3 - 0,2
 

COPPER - ZINC ALLOYS COMPLEX

Material Designation Composition in % (mass fraction) Density g/cm3
 Symbolic  Numerical element Cu Al Fe Mn Ni Pb Si Sn Zn Total other  approx.
CuZn35Ni3Mn2AlPb CW710R min. 58 0,3 - 1,5 2 0,2 - - Rest - 8,3
max 60 1,3 0,5 2,5 3 0,8 0,1 0,5 - 0,3
CuZn36Sn1Pb CW712R min. 61 - - - - 0,2 - 1 Rest - 8,3
max 63 - 0,1 - 0,2 0,6 - 1,5 - 0,2
CuZn37Mn3Al2PbSi CW713R min. 57 1,3 - 1,5 - 0,2 0,3 - Rest - 8,1
max 59 2,3 1 3 1 0,8 1,3 0,4 - 0,3
CuZn37Pb1Si1 CW714R min. 59 - - - - 0,4 - 0,5 Rest - 8,4
max 61 - 0,1 - 0,3 1 - 1 - 0,2
CuZn39Mn1AlPbSi CW718R min. 57 0,3 - 0,8 - 0,2 0,2 - Rest - 8,2
max 59 1,3 0,5 1,8 0,5 0,8 0,8 0,5 - 0,3
CuZn39Sn1 CW719R min. 59 - - - - - - 0,5 Rest - 8,4
max 61 - 0,1 - 0,2 0,2 - 1 - 0,2
CuZn40Mn1Pb1 CW720R min. 57 - - 0,5 - 1 - - Rest - 8,3
max 59 0,2 0,3 1,5 0,6 2 0,1 0,3 - 0,3
CuZn40Mn1Pb1AlFeSn CW721R min. 57 0,3 0,2 0,8 - 0,8 - 0,2 Rest - 8,3
max 59 1,3 1,2 1,8 0,3 1,6 - 1 - 0,3
CuZn40Mn1Pb1FeSn CW722R min. 56,5 - 0,2 0,8 - 0,8 - 0,2 Rest - 8,3
max 58,5 0,1 1,2 1,8 0,3 1,6 - 1 - 0,3
CuZn40Mn2Fe1 CW723R min. 56,5 - 0,5 1 - - - - Rest - 8,3
max 58,5 0,1 1,5 2 0,6 0,5 0,1 0,3 - 0,4

LEAD-FREE BRASS

EN DIN ASTM BS JIS SN
SYMBOLIC NUMERICAL SYMBOLIC NUMERICAL
CuZn5 CW500L CuZn5 2.0220 C21000 - C2100 CuZn5
CuZn10 CW501L CuZn10 2.0230 C22000 CZ101 C2200 CuZn10
CuZn15 CW502L CuZn15 2.0240 C23000 CZ102 C2300 CuZn15
CuZn20 CW503L CuZn20 2.0250 C24000 CZ103 C2400 CuZn20
CuZn28 CW504L CuZn28 2.0261 - - . CuZn28
CuZn30 CW505L CuZn30 2.0265 C26000 CZ106 C2600 CuZn30
CuZn33 CW506L CuZn33 2.0280 C26800 CZ107 C2680 -
CuZn36 CW507L CuZn36 2.0335 C27000 CZ108 C2700 CuZn36
CuZn37 CW508L CuZn37 2.0321 C27200 CZ108 C2700 CuZn37
CuZn40 CW509L CuZn40 2.0360 C28000 CZ109 C2800 CuZn40
 

LEADED BRASS

EN DIN ASTM BS JIS SN
SYMBOLIC NUMERICAL SYMBOLIC NUMERICAL
CuZn37Pb0,5 CW604N CuZn37Pb0,5 2.0332 C33500 - - CuZn37Pb0,5
CuZn35Pb1 CW600N CuZn36Pb1,5 2.0331 C34000 CZ118 C3501 CuZn36Pb1
CuZn35Pb2 CW601N CuZn36Pb1,5 2.0331 C34200 CZ119 - CuZn35Pb2
C34500 CZ131
CuZn37Pb1 CW605N - - C35000 CZ131 C3501 -
CuZn37Pb2 CW606N - - C35300 CZ131 C3601 CuZn37Pb2
CuZn36Pb2As CW602N - - C35330 CZ132 - -
CuZN36Pb3 CW603N 2.0375 CuZn36Pb3 C36000 CZ124 C3601 CuZn36Pb3
C3602
CuZn38Pb4 CW609N - - - CZ121/4 C3605 -
CuZn39Pb0,5 CW610N CuZn39Pb0,5 2.0372 C36500 CZ123 - CuZn39Pb0,5
CuZn38Pb1 CW607N - - C37000 CZ129 C3501 CuZn38Pb1
CuZn38Pb2 CW608N - - C37700 CZ128 - CuZn38Pb2
CuZn39Pb2 CW612N CuZn39Pb2 2.0380 C37700 CZ128 C3771 CuZn39Pb2
CuZn40Pb2 CW617N CuZn40Pb2 2.0402 C37800 CZ120 C3603 CuZn40Pb2
C38000 C3604
CuZn43Pb2Al CW624N CuZn44Pb2 2.0410 C38000 - - -
CuZn39Pb3 CW614N CuZn39Pb3 2.0401 C38500 CZ121/3 C3603 CuZn39Pb3
C3604
CuZn40Pb1Al CW616N - - - - - CuZn40Pb1
CuZn42PbAl CW621N - - - - - -
CuZn39Pb1 CW719R CuZn38Sn1 3.0530 C46400 CZ133 - CuZn38Sn1
CuZn31Si CW708R CuZn31Si 2.0490 - - - -
CuZn37Mn3Al2PbSi CW713R CuZn40Al2 2.0550 C67410 CZ 135 - CuZn40Al2
CuZn35Ni3Mn2AlPb CW710R CuZn35Ni 2.0540 - - - -
CuZn40Mn1Pb1 CW720R CuZn40Mn1Pb 2.0580 - CZ136 - CuZn40Mn1Pb1
CuZn40Mn2Fe1 CW723R CuZn42Mn2 2.0572 - - - CuZn42Mn2
CuZn20Al2As CW702R CuZn20Al2 2.0460 C68700 CZ110 C6870 -
Designations Nominal dimension of the cross section Tensile Strength Rm N/mm2 min. Yield limit at 0,2% Rp0.2 N/mm2 approx. Elongation A % approx. Hardness
Material profilea Rectangular plate thickness mm HB min. HV min.
Symbolic Numerical Metallurgical State from up to and including
M All All Manufacturing gross
CuZn38Pb1 CuZn38Pb2 CuZn39Pb0,5 CuZn39Pb1 CuZn39Pb2 CuZn39Pb2Sn CW607N CW608N CW610N CW611N CW612N CW613N
R460 - - 6 460 (320) (8) - -
H120 - - 6 - - - 120 125
R410 - 6 60 410 (190) (20) - -
H105 - 6 60 - - - 105 110
CuZn38Pb4 CuZn39Pb3 CuZn40Pb2 CuZn40Pb2Sn CuZn43Pb2 CW609N CW614N CW617N CW619N CW623N M All All Manufacturing gross
R480 - - 6 480 (330) (5) - -
H130 - - 6 - - - 130 135
R430 - 6 60 430 (200) (15) - -
H110 - 6 60 - - - 110 115
CuZn35Pb1 CuZn35Pb1 CuZn36Pb3 CuZn37Pb2 CW600N CW601N CW603N CW606N M All All Manufacturing gross
R440 - - 6 440 (300) (10) - -
H115 - - 6 - - - 115 120
R400 - 6 60 400 (180) (25) - -
H100 - 6 60 - - - 100 105
CuZn36Pb2As CW602N M All All Manufacturing gross
R350 - - 6 350 (240) (15) - -
H110 - - 6 - - - 110 115
R280 - 6 60 280 (130) (30) - -
H080 - 6 60 - - - 80 85
CuZn38Pb1 CuZn38Pb2 CuZn39Pb0,5 CuZn39Pb1 CuZn39Pb2 CuZn39Pb2Sn CW607N CW608N CW610N CW611N CW612N CW613N M All All Manufacturing gross
R460 - - 6 460 (320) (8) - -
H120 - - 6 - - - 120 125
R410 - 6 60 410 (190) (20) - -
H105 - 6 60 - - - 105 110
CuZn38Pb4 CuZn39Pb3 CuZn40Pb2 CuZn40Pb2Sn CuZn43Pb2 CW609N CW614N CW617N CW619N CW623N M All All Manufacturing gross
R480 - - 6 480 (330) (5) - -
H130 - - 6 - - - 130 135
R430 - 6 60 430 (200) (15) - -
H110 - 6 60 - - - 110 115
CuZn40Pb2Al CuZn41Pb1Al CuZn42PbAl CuZn43Pb1Al CuZn43Pb2Al CW618N CW620N CW621N CW622N CW624N M All All   Manufacturing gross        
a Para estos perfiles, las características mecánicas dependerán de la forma y dimensiones del perfil y estarán sometidas a acuerdo entre el cliente y suministrador.
NOTA 1 - Los valores entre paréntesis no son requisitos de esta norma, se dan sólo como información.
NOTA 2 - 1N/mm2 is equivalent to 1 Mpa.
Nominal thickness Tolerances on thinckness, for nominal widths of
Greater than Up to and including Width tolerance From 3 to 6 inclusive Greater than 6 to 10 inclusive Greater than 10 to 18 inclusive Greater than 18 to 30 inclusive Greater than 30 to 50 inclusive Greater than 50 to 60 inclusive
Class A tolerance
6a 18 ± 0,27 ± 0,18 ± 0,22 ± 0,27 - - -
18 30 ± 0,33 ± 0,18 ± 0,22 ± 0,27 ± 0,33 - -
30 50 ± 0,62 ± 0,22 ± 0,27 ± 0,33 ± 0,45 ± 0,62 -
50 80 ± 1,20 ± 0,27 ± 0,33 ± 0,45 ± 0,52 ± 0,74 ± 1,00
80 120 ± 2,20 ± 0,33 ± 0,45 ± 0,52 ± 0,74 ± 1,00 ± 1,20
Class B tolerance
6a 18 ± 0,15 ± 0,10 ± 0,12 ± 0,15 - - -
18 30 ± 0,22 ± 0,10 ± 0,12 ± 0,15 ± 0,22 - -
30 50 ± 0,30 ± 0,13 ± 0,15 ± 0,18 ± 0,22 ± 0,30 -
50 80 ± 0,37 ± 0,16 ± 0,18 ± 0,22 ± 0,30 ± 0,37 -
80 120 ± 0,45 ± 0,18 ± 0,22 ± 0,27 ± 0,35 ± 0,45 -
Class C tolerance
6a 18 ± 0,10 ± 0,07 ± 0,09 ± 0,10 - - -
18 30 ± 0,15 ± 0,07 ± 0,09 ± 0,10 ± 0,15 - -
30 50 ± 0,20 ± 0,09 ± 0,10 ± 0,12 ± 0,15 ± 0,20 -
50 80 ± 0,25 ± 0,11 ± 0,12 ± 0,15 ± 0,20 ± 0,25 -
80 120 ± 0,30 ± 0,12 ± 0,15 ± 0,18 ± 0,23 ± 0,35 -
a included in 6.

Documentation download

Title
Other languages
Type
Created
INDUSTRIAL SECTOR Bronmetal
Type Catalogue
Created 07/07/2020
You may also like

Flat copper bar / rectangular bar

Brass tubes

Brass profiles
Linkedin
Contact
Sectors
Electrical
Industrial
Downloads
Catalogues
Technical data sheets
Certifications
Documentation
Tools
Weight and lenght calculator
News
News
Copyright © 2024 Bronmetal.
Legal Notice
Privacy Policy
Cookies Policy
General conditions of sale

More products...

More products...